Tecoform® PO20 GR20 NL HS
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecoform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LAfoHr_Tecoform-PO20-GR20-NL-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM, 20% glass fiber reinforced, heat stabilized, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.7 | % | |
| Flow | 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 155 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Hopper Temperature | 30.0 to 50.0 | °C | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 80.0 to 100 | MPa | |
| Back Pressure | Low |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARC ARC6604 | ARC Resin Corporation | Nylon 66 | ARC |
| Flexoprene® 85 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |
| KumhoSunny ABS HU600 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| MAJORIS ET370 | AD majoris | PP, Unspecified | MAJORIS |
| OTECH PVC PL1001-8 - Plenum Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |