KumhoSunny SMA HSG5415
| Category: | SMA , Styrene Maleic Anhydride |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny SMA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LAIwqF_KumhoSunny-SMA-HSG5415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HSG5415 is an 15% glass fiber reinforced SMA alloy,offering high heat resistance,high modulus and low odour. Application:automobile interiors and exteriors such as instrument Panel, console substrate, instrument panel ducts, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/5.0 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.30 to 0.50 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 73.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 5000 | MPa | ISO 178 |
| Flexural Stress 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | 30 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength 5(23°C) | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed) | 117 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 105 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Nozzle Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G30 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Borealis PE CT7200 | Borealis AG | PE Homopolymer | Borealis PE |
| Hifax EKC 107X | LyondellBasell Industries | PP Copolymer | Hifax |
| TOLEN H038 TF/2 | SIBUR | PP Homopolymer | TOLEN |
| PENTAMID B GV35 H black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |