EPO-TEK® OE101
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L9rcgw_EPO-TEK-OE101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component epoxy designed for low stress applications in fiber optic packaging, opto-electronics and semiconductors. It is a lower modulus version of EPO-TEK® 353ND. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| K+ | 7 | ppm | |
| Na+ | 6 | ppm | |
| NH4+ | 171 | ppm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 456 | °C | |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 2.47 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.60 | % | |
| 250°C | 0.82 | % | |
| 300°C | 1.2 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 65.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.1E-5 | cm/cm/°C | |
| -- 3 | 2.1E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.546 | ||
| Transmittance | |||
| 400 nm | > 50.0 | % | |
| 600 nm | > 92.0 | % | |
| 675 nm | > 97.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | Transparent, Light Yellow | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.16 | g/cm³ | |
| Viscosity 7(23°C) | 1.5 to 2.5 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 240 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.22 | ||
| Volume Resistivity (23°C) | > 1.5E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 3.6E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SD-0150UF | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Geon™ Vinyl Rigid Extrusion 87564 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| HM10® Max | Heritage Plastics, Inc. | LLDPE | HM10® |
| OTECH PVC OW842 - Riser Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| 3M™ Dyneon™ PTFE Compound TF 3236 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |