Desmovit® DP R 3914
| Category: | TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether) |
| Manufacturer: | geba Kunststoffcompounds GmbH |
| Trademark: | Desmovit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L98r8G_Desmovit-DP-R-3914.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High stiffness, very good impact resistance and flexibility even at low temperatures - these are the strengths of new glass fibre reinforced polyetherdiol based thermoplastic polyurethanes (TPUs). |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | |||
| Across Flow | 0.11 | % | |
| Flow | 0.36 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 58.0 | MPa | ISO 527-2/200 |
| Tensile Strain (Break) | 23 | % | ISO 527-2/200 |
| Flexural Modulus 1 | ISO 178 | ||
| -30°C | 3620 | MPa | |
| 23°C | 1370 | MPa | |
| Flexural Stress 2 | ISO 178 | ||
| -30°C | 129 | MPa | |
| 23°C | 43.0 | MPa | |
| Abrasion | 65 | mm³ | ISO 4649 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 162 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B50 |
| CLTE | DIN 53752 | ||
| Flow | 9.0E-6 | cm/cm/°C | |
| Transverse | 1.4E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 200 to 245 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GF 30 2 black (2211) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| CERTENE™ HI-355 | Muehlstein | HDPE | CERTENE™ |
| Edgetek™ PK-30GF/000 EM NC | PolyOne Corporation | PEEK | Edgetek™ |
| Paxon™ EA55-003 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |
| Sylvin 8486-75LG Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |