TOTAL Polystyrene Compound 260-50
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L90tGI_TOTALPolystyreneCompound26050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL POLYSTYRENE 260-50 is an easy flow, high impact polystyrene for injection molding application. 260-50 contains a significant level of recycled polystyrene. This grade is recommended for manufacturing of articles which require good dimensional stability. Applications
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 25 | % | ISO 527-2 |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Dielectric Strength | 160 | kV/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | < 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2825 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| CYCOLOY™ C6200 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| E-RIALFILL H 15 D 20 T | RIALTI Srl | PP Homopolymer | E-RIALFILL |
| ESPRENE EPDM 301 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| LUVOCOM® 19-7748 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |