Geon™ Vinyl Dry Blend E6950
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Dry Blend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L8mqPK_Geon-Vinyl-Dry-Blend-E6950.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ Vinyl Dry Blend E6950 is a Rigid Polyvinyl Chloride product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Plumbing/Piping/Potable Water. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-41443-33-0000 | ASTM D4216 | |
| PVC Cell Classification | 16354 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2760 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 46.9 | MPa | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact - Across Flow (23°C, 3.18 mm, Compression Molded) | 1100 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 57.8 | J/cm | |
| 23°C 4 | 200 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 3.18 mm, Compression Molded) | 73.9 | °C | ASTM D648 |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 5VA | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Procedure A, C.125 Dart |
| 4 . | Procedure B, C.125 Dart |
| 5 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MonoSol® M8440 | MonoSol, LLC | PVOH | MonoSol® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| ESTAPROP K 1060 TG | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Pinnacle PP 1355Z | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |
| Vipel® K010-TBD-30 | AOC, L.L.C. | Vinyl Ester | Vipel® |