HAIPLEN H30 G5
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L7XKIc_HAIPLEN-H30-G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer glass fiber reinforced 25%. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 to 0.60 | % | |
| Across Flow | 0.80 to 0.90 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 155 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 115 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 100 | °C | ASTM D1525, ISO 306/B 3 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (3.20 mm) | 650 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 7051SS | Resinoid Engineering Corporation | Phenolic | Resinoid |
| TRIMID® N66-G43HL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Adell PE KV-11-N | Adell Plastics, Inc. | HDPE | Adell PE |
| Geon™ Fiberloc™ 80520 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |
| Elastocon® 2840ST | Elastocon TPE Technologies | TPE | Elastocon® |