Ultradur® B 2300 G6 HR Unc.
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L7PbX6_Ultradur-B-2300-G6-HR-Unc-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur B 2300 G6 HR Unc. is a hydrolysis resistant, 30% fiberglass reinforced PBT, exhibiting superior flow characteristics. Designed for improved latch strength in automotive connectors. Applications Ultradur B 2300 G6 HR Unc. was developed for thin walled automotive connectors designed to meet USCAR Class III requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Viscosity Number (Reduced Viscosity) | 90.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 136 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 198 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 73 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| CLTE | |||
| Flow | 1.7E-5 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502-A Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| VECTRA® V143XL | Celanese Corporation | LCP | VECTRA® |
| ULTEM™ JD7903 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| ARCEL® 730 (1.50 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| HIDEN® HT306 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |