CONTINUUM™ DGDC-2482 NT
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L7PHYv_CONTINUUM-DGDC-2482-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONTINUUM™ DGDC-2482 NT Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long-term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation are desired. Suitable applications include natural gas distribution pipes, large diameter industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance: ASTM D 3350: cell classification
NOTES: (1) Natural resin extruded under proper conditions with Dow-approved carbon black masterbatch (6.5%). |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| Natural | 0.949 | g/cm³ | |
| Black 1 | 0.959 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 6.8 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | > 24.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790B |
| Hydrostatic Strength 4 | ASTM D1598 | ||
| 1798 psi (12.4 MPa) : 20°C | > 100 | hr | |
| 798 psi (5.5 MPa) : 80°C | > 1000 | hr | |
| Resistance to Rapid Crack Propagation, Pc 5 | > 12.0 | bar | ISO 13477 |
| Resistance to Rapid Crack Propagation, Tc 6 | < -17 | °C | ISO 13477 |
| Slow Crack Growth PENT 7 | > 5000 | hr | ASTM F1473 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability | > 220 | °C | ASTM D3350 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 8(23°C) | 490 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 9 | < -75.0 | °C | ASTM D746A |
| Note Message | |
|---|---|
| 1 . | Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%) |
| 2 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 3 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 4 . | Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%) |
| 5 . | 3Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%)Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 6 . | 3Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 BK (6.5%)Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 7 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 8 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 9 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PC2320.F | Guangdong Silver Age Sci & Tech. Co., Ltd | PC | SILVER® |
| MORETEC™ 0248Z | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| AMTOPP IM25 | Inteplast Group | PP, Unspecified | AMTOPP |
| Evoprene™ GC 5659 | AlphaGary | SEBS | Evoprene™ GC |
| LUVOCOM® 1301-VAP 10 | LEHVOSS Group | PPS | LUVOCOM® |