Product Profile:
PLEXIGLAS® Resist zk5HF is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

high weather resistance

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk5HF is characterized by the following special properties:

high break resistance and impact strength

improved resistance to stress cracking

excellent flow.

Application:
Used for injection molding as well as for extruding sheets and profiles.

Examples:
applications involving thin walls and long flow paths; thin-walled components; items requiring accurate mold surface reproduction, such as very finely textured luminaire covers.

General Information
Additive	Impact Modifier
Features	Good Flow Good Weather Resistance High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Molds/Dies/Tools Protective Coverings Sheet Textile Applications Wall Panels
Forms	Pellets
Processing Method	Extrusion Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.17	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	8.10	cm³/10min	ISO 1133
Water Absorption			ISO 62
23°C, 24 hr	1.9	%
Equilibrium, 23°C, 50% RH	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2/1
Tensile Stress (Yield)	55.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	4.5	%	ISO 527-2/50
Nominal Tensile Strain at Break	25	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	50	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	96.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	9.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	< 85.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
RANPELEN SEP-750	Lotte Chemical Corporation	PP Terpolymer	RANPELEN
SuperLite XLT® SLXLTA.0641BZ	Azdel, Inc.	PP, Unspecified	SuperLite XLT®
ALCOM® PA6 900/5 CF/MR	ALBIS PLASTIC GmbH	Nylon 6	ALCOM® PA6
LEXAN™ HF500R resin	SABIC Innovative Plastics Europe	PC	LEXAN™
Sylvin 9915-85 NATURAL	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin