LNP™ STAT-KON™ WX06322 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L5lldi_LNP-STAT-KON-WX06322-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CF filled low warpage PBT Grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.17 | % | |
| Across Flow | 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (6.40 mm) | 11500 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 202 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 204 | °C | ASTM D648 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.3E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® RT51 | A. Schulman Europe | ABS | RONFALIN® |
| Nipol® BR 1220SG | Zeon Corporation | PBR, High Cis | Nipol® BR |
| CP PRYME® PC/ABS PCA100 | Chase Plastics Services Inc. | PC+ABS | CP PRYME® PC/ABS |
| Daelim Po1y® PP-137V | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Ferro PE NPE00IA04NA | Ferro Corporation | PE, Unspecified | Ferro PE |