PROTEQ™ C25SK9
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L5RZxr_PROTEQ-C25SK9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C25SK9 is a medium flow, heat stabilised flame retardant grade of Polypropylene copolymer for applications where long term heat aging stability and flame retardant are required. PPC25SK9 is designed to meet the stringent UL94 V-2 and AS/NZS 60695.2.12 (IEC 60695-2-12) 960°C Glow Wire flammability test. Typical applications include light fittings, electrical appliances where an elevated temperature is expected and a high level of flame retardancy is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.979 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1600 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 38.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 70 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | > 850 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 8.00 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 7531 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| SynPlast™ MXP | PolyOne Corporation | Mixed Alkyl Phthalate | SynPlast™ |
| Clariant Nylon 6/6 6642-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Ferro PP NPP00GC25WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Petrothene® L3035 | LyondellBasell Industries | LDPE | Petrothene® |