CP PRYME® Nylon 66 NN100LZ-7
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® Nylon 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L4iIeD_CPPRYMENylon66NN100LZ7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime Nylon 6/6, High Rigidity & Toughness, Lubricated, FDA Compliant, Injection Molding Grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Lateral flow : 23°C, 2.00mm | 2.0 | -- | % | ISO 294-4 |
| Traffic : 23°C, 2.00mm | 2.0 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3300 | 1600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 88.3 | 55.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 60.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3300 | 1050 | MPa | ISO 178 |
| Flexural Stress (23°C) | 105 | 30.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 6.9 | kJ/m² | ISO 179/1eA |
| 23°C | 6.1 | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 5.0 | 6.9 | kJ/m² | ISO 180 |
| 23°C | 6.1 | 23 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.2 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.40 mm | 130 | -- | °C | UL 746 |
| 0.71 mm | 130 | -- | °C | UL 746 |
| 1.5 mm | 130 | -- | °C | UL 746 |
| 3.0 mm | 130 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.40 mm | 75.0 | -- | °C | UL 746 |
| 0.71 mm | 75.0 | -- | °C | UL 746 |
| 1.5 mm | 75.0 | -- | °C | UL 746 |
| 3.0 mm | 75.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.40 mm | 75.0 | -- | °C | UL 746 |
| 0.71 mm | 85.0 | -- | °C | UL 746 |
| 1.5 mm | 85.0 | -- | °C | UL 746 |
| 3.0 mm | 85.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.749 mm) | 1.0E+10 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 26 | -- | kV/mm | IEC 60243-1 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.71 mm | PLC 0 | -- | UL 746 | |
| 1.5 mm | PLC 0 | -- | UL 746 | |
| 3.0 mm | PLC 0 | -- | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.71 mm | PLC 4 | -- | UL 746 | |
| 1.5 mm | PLC 3 | -- | UL 746 | |
| 3.0 mm | PLC 3 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | V-2 | -- | UL 94 | |
| 0.71 mm | V-2 | -- | UL 94 | |
| 1.5 mm | V-2 | -- | UL 94 | |
| 3.0 mm | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.71 mm | 799 | -- | °C | IEC 60695-2-12 |
| 1.5 mm | 799 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 932 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.71 mm | 699 | -- | °C | IEC 60695-2-13 |
| 1.5 mm | 699 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 699 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 70 | °C | |
| Drying Time | 1.0 - 3.0 | hr | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 285 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 285 - 300 | °C | |
| Mold Temperature | 65 - 95 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW250F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TAROBLEND 66 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| THERMALGRAPH® EWC-600X | Cytec Industries Inc. | Carbon/Epoxy | THERMALGRAPH® |
| BLUESTAR® PBT 201G25 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Sylvin 7833-85 White 1574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |