Tecnoprene® 3K4ELU1 NERO900
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L3l6Pw_Tecnoprene-3K4ELU1-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastomer modified polypropylene copolymer reinforced with 20% chemically coupled glass fiber, high UV resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.35 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 119 | °C | ASTM D648 |
| Vicat Softening Temperature | 74.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hipolyene 8110 | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Karina BROWN PVC COMPOUND 800-36/266-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GREEN COLOR CONCENTRATE 40/130-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pebax® MV 1074 SP 01 | Arkema | PEBA-Ether | Pebax® |
| Complet® LCF10-LGF20-PP | PlastiComp, Inc. | PP Homopolymer | Complet® |