MAJ'ECO CEP460W
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L3VfdA_MAJ-ECO-CEP460W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO CEP460W is a 40% wood fibre reinforced polypropylene compound intended for injection moulding. MAJ'ECO CEP460W has been developed especially for demanding applications in various engineering sectors. MAJ'ECO CEP460W is modified elastomer. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1190 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 7.2 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1450 | MPa | ISO 178 |
| Flexural Stress 2 | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 26 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 7 FR 4 K1681 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Toyolac® 450Y MH5 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| CERTENE™ LLBF-122F | Muehlstein | LLDPE | CERTENE™ |
| COPYLENE® CR350CL-01 | Phillips 66 | PP Random Copolymer | COPYLENE® |
| KYOCERA TCG5910 | KYOCERA Chemical Corporation | TS, Unspecified | KYOCERA |