ULTEM™ 1010FC resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L3CPG9_ULTEM-1010FC-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ULTEM 1010FC resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM 1010FC resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures with easy flow. This grade is US FDA and EU Food Contact compliant. ULTEM 1010FC resin is not supported with biocompatibility information. For medical applications which require biocompatibility we offer ULTEM HU1010 resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (340°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.3 | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 105 | MPa | |
| Break | 85.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 60 | % | |
| Flexural Modulus 2 | 3300 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 195 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 190 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 211 | °C | ISO 306/B50 |
| -- | 212 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 5.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI Str | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.60 mm, in Oil) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | ||
| 60 Hz | 2.90 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 5.0E-4 | ||
| 60 Hz | 5.0E-4 | ||
| 1 MHz | 6.0E-3 | ||
| 2.45 GHz | 2.5E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 150 | V | |
| Solution B | 100 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 47 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 to 120 | °C | |
| Rear Temperature | 350 to 400 | °C | |
| Middle Temperature | 360 to 410 | °C | |
| Front Temperature | 370 to 420 | °C | |
| Nozzle Temperature | 360 to 410 | °C | |
| Processing (Melt) Temp | 370 to 410 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3887 | RTP Company | PAEK | RTP |
| Shinko-Lac® ABS 7001 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Vi-Chem PVC VNC87-5E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Chemical Resources PA612153HS | Chemical Resources, Inc. | Nylon 612 | Chemical Resources |
| Dryflex® 600861 | ELASTO | TPE | Dryflex® |