Ferro PP TPP40AC46BK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L2oYSE_Ferro-PP-TPP40AC46BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP TPP40AC46BK is a Polypropylene Homopolymer (PP Homopolymer) material filled with 43% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Important attributes of Ferro PP TPP40AC46BK are:
Typical application of Ferro PP TPP40AC46BK: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 | % | |
| Across Flow | 1.3 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 3230 | MPa | |
| Tangent : 23°C | 3620 | MPa | |
| Flexural Strength (23°C) | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 210 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 0.791 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 129 | °C | |
| 1.8 MPa, Unannealed | 79.4 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 210 | °C | |
| Middle Temperature | 210 to 213 | °C | |
| Front Temperature | 213 to 216 | °C | |
| Nozzle Temperature | 216 to 218 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® COC P15P | Tekni-Films, a div of Tekni-Plex | Film, PP/COC/PP | TEKNIFLEX® |
| 3M™ Dyneon™ PTFE Compound TF 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Bayblend® FR3005 BBS310 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Crastin® LW9330 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| OTECH PVC OW837 GPT - Automotive Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |