AvaSpire® AV-755 SL45
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L2KUCs_AvaSpire-AV-755-SL45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AV-755 SL45 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates and high pressure-velocity (PV) tolerance in lubricated wear environments. Like the other members of the AvaSpire® AV-700 series, AV-755 SL45 offers more attractive economics than PEEK while retaining most of PEEK's key attributes. In addition to the outstanding wear resistance, the resin also offers the outstanding combination of chemical resistance, mechanical strength and stiffness at elevated temperatures, as well as long-term and high temperature thermal-oxidative stability. AV-755 SL45 is formulated with a binary anti-friction/anti-wear additive system comprised of carbon fiber and graphite. By virtue of its additive system, this resin also offers, exceptionally high stiffness and very low moisture absorption. Potential applications for AV-755 SL45 include bushings, bearings, wear strips, wear rings, rollers, and other parts used in sliding friction components. This high flow (low viscosity) resin is black. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18mm | 0.0 - 0.20 | % | ASTM D955 |
| Transverse flow : 3.18mm | 1.2 - 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 33600 | MPa | ASTM D638 |
| -- | 30400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 173 | MPa | ISO 527-2/1A/5 |
| -- 3 | 169 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 4 | 0.90 | % | ASTM D638 |
| Fracture | 0.90 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 25900 | MPa | ASTM D790 |
| -- | 30200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 250 | MPa | ASTM D790 |
| -- | 266 | MPa | ISO 178 |
| Compressive Strength | 120 | MPa | ASTM D695 |
| Shear Strength | 70.0 | MPa | ASTM D732 |
| Coefficient of Friction | ASTM D3702 | ||
| -- 5 | 0.050 | ASTM D3702 | |
| -- 6 | 0.12 | ASTM D3702 | |
| -- 7 | 0.34 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 53 | J/m | ASTM D256 |
| -- | 6.8 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 320 | J/m | ASTM D4812 |
| -- | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 8(1.8 MPa, Annealed, 3.20 mm) | 278 | °C | ASTM D648 |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Peak Melting Temperature | 343 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 7.0E-6 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1170 | J/kg/°C | DSC |
| 200°C | 1610 | J/kg/°C | DSC |
| Thermal Conductivity | 0.70 | W/m/K | ASTM E1530 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 600 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 354 | °C | |
| Middle Temperature | 366 | °C | |
| Front Temperature | 371 | °C | |
| Nozzle Temperature | 374 | °C | |
| Processing (Melt) Temp | 366 - 388 | °C | |
| Mold Temperature | 149 - 177 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Back Pressure: Minimum |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | Lubrication conditions: 800 fpm , 750 psi (6.06 m/s , 5171 kPa) |
| 6 . | Lubrication conditions: 75 fpm, 1000 psi (0.38 m/s , 6895 kPa) |
| 7 . | Drying conditions: 800 fpm,31.25 psi (4.06 m/s,215 kPa). 50 fpm,500 psi (0.25 m/s,3447 kPa) is not recommended. |
| 8 . | 200°C,2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V967 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| UBESTA 3030JFX3 | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| CERTENE鈩?PBM-10 | Muehlstein | PP Impact Copolymer | CERTENE™ |
| ENVIROPLAS® ENV12-NC220 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| Stat-Tech™ ST6000-5006 FR BLACK X3 | PolyOne Corporation | Nylon 6 | Stat-Tech™ |