Quadrant EPP Nylon 101
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L1IzPZ_Quadrant-EPP-Nylon-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 101 is an extruded form of polyamide, offering rigidity, strength, wear resistance, and heat resistance to 210°F. It is commonly used in both structural and general-purpose bearing and wear applications. This material is available in natural and black. The natural material is compliant with FDA, USDA, NST, and 3A-Dairy regulations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.30 | % | |
| Saturation | 7.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 85 | ||
| R-Scale | 115 | ||
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2930 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Compressive Modulus | 2900 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 86.2 | MPa | ASTM D695 |
| Shear Strength | 68.9 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.25 | Internal Method | |
| Wear Factor | 160 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 99 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.0946 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 260 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 9.9E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP CPC35C | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PP |
| MEGOLON™ S380 | AlphaGary | TP, Unspecified | MEGOLON™ |
| Tenac™-C TFC77 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Stanyl® TW241B3 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Zythane® 5070A | Alliance Polymers & Services | TPU-Polyester | Zythane® |