Plexiglas® Heatresist FT15
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L1GQow_Plexiglas-Heatresist-FT15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Profile: PLEXIGLAS® Heatresist FT15 is a special acrylic-based polymer. With regard to its
PLEXIGLAS® Heatresist FT15 shows comparable properties to those of PLEXIGLAS® standard molding compounds. In addition, PLEXIGLAS® Heatresist FT15 offers the special benefit of a
Application: PLEXIGLAS® Heatresist FT15 is particularly suitable for injection moldings. Examples: luminaire covers, automotive lights and technical moldings exposed to high temperatures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 4.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 107 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Glass Transition Temperature | 121 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 115 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 675 | °C | IEC 60695-2-13 |
| Fire Rating | B2 | DIN 4102 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.502 | ISO 489 | |
| Transmittance 1 | 91.0 | % | ISO 13468-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 70.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | D65 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 2315 | Huntsman Corporation | PAO | REXtac® APAO |
| Texalan® 4 Series 490A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |
| EZPrene 9050D | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| FHR Polypropylene AP5135-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Magnobond 79-3 | Magnolia Plastics, Inc. | Epoxy | Magnobond |