Cereplast Compostables® 1001
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Compostables® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L0nxz5_Cereplast-Compostables-1001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 1001, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 1001 has been designed to have an excellent balance of toughness, rigidity and processability. Compostable 1001 can be processed on existing conventional electric and hydraulic reciprocating screw injection molding machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3590 | MPa | ASTM D638 |
| Tensile Strength (Break) | 49.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.1 | % | ASTM D638 |
| Flexural Modulus | 3360 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 33 | J/m | ASTM D256 |
| Dart Drop Impact | 1.13 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 44.4 | °C | ASTM D648B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 163 - 177 | °C | |
| Middle Temperature | 177 - 191 | °C | |
| Front Temperature | 177 - 204 | °C | |
| Nozzle Temperature | 177 - 204 | °C | |
| Processing (Melt) Temp | 174 - 204 | °C | |
| Mold Temperature | 10.0 - 26.7 | °C | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Material Drying Temp (regrind): 100 to 120°F (4 hrs.) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBB3713 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| DENIFORM 2010 | Vamp Tech | Acetal (POM) Copolymer | DENIFORM |
| Dryflex® 50225 | ELASTO | TPE | Dryflex® |
| OxyVinyls® 185F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |