LNP™ LUBRICOMP™ WL002 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L0XzCx_LNP-LUBRICOMP-WL002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WL002 is a compound based on PBT resin containing 10% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound WL-4020 Product reorder name: WL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2780 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/5 |
| Break 3 | 51.0 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 9.3 | % | ASTM D638 |
| Yield | 9.8 | % | ISO 527-2/5 |
| Break 5 | 12 | % | ASTM D638 |
| Break | 11 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2640 | MPa | ASTM D790 |
| -- 7 | 2340 | MPa | ISO 178 |
| Flexural Stress | 78.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.35 | ||
| vs. Itself - Static | 0.31 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 2.75 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 25.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 39 | J/m | ASTM D256 |
| 23°C 8 | 3.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 880 | J/m | ASTM D4812 |
| 23°C 9 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.68 | J | ASTM D3763 |
| -- | 0.700 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 182 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 160 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 58.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 57.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 TFE 20 | RTP Company | ABS | RTP |
| TRISTAR® PC-10R-CL(6) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Cleapact TS-50 | DIC Corporation | SBC | Cleapact |
| Karina GRAY PVC COMPOUND 853-18/233-DY-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECHNYL STAR® S 60G1 V30 NATURAL LP | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |