Elastamax™ XL-2155
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Elastamax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kzi1xN_Elastamax-XL-2155.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Elastamax™ XL thermoplastic olefins (TPOs) are based on pelletized blends of polyolefin resins and select elastomers such EPDM. These materials have been engineered to provide a balance of physical properties and processability, and are an economical alternative to traditional thermoset rubber and more costly thermoplastic elastomers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 52 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412A | ||
| 100% Strain | 6.14 | MPa | |
| 300% Strain | 8.34 | MPa | |
| Tensile Strength 2(Break) | 8.76 | MPa | ASTM D412A |
| Tensile Elongation 3(Break) | 370 | % | ASTM D412A |
| Tear Strength 4 | 19.3 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 36 | % | ASTM D395B |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 20 FR NATURAL | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Trithene® TS 7045 | Petroquimica Triunfo | LDPE | Trithene® |
| Hypro® PP-HP 12NS | Entec Polymers | PP Homopolymer | Hypro® |
| Leona™ 1402S | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| XENOY™ X5630Q resin | SABIC Innovative Plastics Europe | PC+PET | XENOY™ |