REPOL® C200MN
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KyxMGL_REPOL-C200MN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol C200MN is recommended for use in Injection Moulded processes where high rigidity and impact strength are required. It is an ideal material to use in collapsible crates, automotive compounds, furniture etc. Repol C200MN contains antistatic agent and nucleating agent for good stiffness. The grade is formulated for lower cycle time. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1200 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 105 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYMAX® GT7058 | Westlake Chemical Corporation | EMA | TYMAX® |
| Adell PS IV-14-N | Adell Plastics, Inc. | PS (HIPS) | Adell PS |
| DESLON™ 66 DSC201GH7 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Generic PP Alloy | Generic | PP Alloy | Generic |
| MAJORIS EB760 | AD majoris | PP, Unspecified | MAJORIS |