Futerro® Fiber Melt Spinning
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Futerro |
| Trademark: | Futerro® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KyFcfa_Futerro-Fiber-Melt-Spinning.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Futerro® PLA polymer is a thermoplastic fiber-grade resin from annually renewable resources. Available in pellet form, it is designed for extrusion into mechanically drawn staple fibers or continuous filament, using conventional fiber spinning and drawing equipment. Futerro® PLA polymer is typically well suited for fiber processes where lower fiber shrinkage is desired: partially orientated yarn (POY), fully drawn yarn (FDY), staple fibers, and continuous filament. It can be converted into a broad range of fiber products Potential applications for Futerro® PLA polymer include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 10 - 15 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 15 - 30 | g/10 min | ISO 1133 |
| Free Lactide Content | % | ||
| L-poly-Lactide Content | > 99 | % | |
| Moisture Content | ppm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 60.0 | MPa | ISO 527-2 |
| Fracture | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 52.0 - 60.0 | °C | ISO 11357-2 |
| Melting Temperature | 145 - 175 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | > 90.0 | % | ISO 14782 |
| Haze (2000 µm) | < 5.0 | % | ISO 14782 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density (230°C) | 1.08 - 1.12 | g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 220 | °C | |
| Cylinder Zone 3 Temp. | 230 | °C | |
| Melt Temperature | 220 - 240 | °C |
| Extrusion instructions |
|---|
| Feed Throat Temperature: 25°CMelt Pump Temperature: 235°CSpin Head Temperature: 235°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Impact 8265 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| GAPEX® RPP30EU24HB BLACK | Ferro Corporation | PP, Unspecified | GAPEX® |
| KOPLA PA66 KDP1000F | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LTP ZC-1180 | Chengdu Letian Plastics Co., Ltd | PPS, Linear | LTP |
| Sylvin 6239-85UV White 1583 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |