Lotader® 4700

Category:	EEA , Ethylene Ethyl Acrylate Copolymer
Manufacturer:	Arkema
Trademark:	Lotader®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ky473O_Lotader-4700.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
LOTADER® 4700 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Acrylic ester brings softness and polarity, while keeping high thermal stability during processing. The high content of acrylic ester leads to high flexibility (low-cristallinity) and high impact absorption behaviour. Maleic anhydride gives reactivity (versus OH and NH 2 groups), leading to optimal dispersion during melt mixing with engineering thermoplastics (mainly polyamides). Applications Due to its properties (softness, reactivity), LOTADER® 4700 is suitable as modifier to improve the impact strength of polyamides (PA6, PA66, PA12 etc.). It can also be used as a compatibilizer for polyamides / polyolefins blends.

Message

LOTADER® 4700 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

Acrylic ester brings softness and polarity, while keeping high thermal stability during processing.

The high content of acrylic ester leads to high flexibility (low-cristallinity) and high impact absorption behaviour.

Maleic anhydride gives reactivity (versus OH and NH 2 groups), leading to optimal dispersion during melt mixing with engineering thermoplastics (mainly polyamides).

Applications
Due to its properties (softness, reactivity), LOTADER® 4700 is suitable as modifier to improve the impact strength of polyamides (PA6, PA66, PA12 etc.). It can also be used as a compatibilizer for polyamides / polyolefins blends.

General Information
Features	Dispersible Good Flexibility Good Thermal Stability High Impact Resistance High Reactivity Non-Corrosive Soft Terpolymer
Uses	Plastics Modification
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	0.940	g/cm³	ISO 1183, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.0	g/10 min	ASTM D1238, ISO 1133
Ethyl Acrylate Content	29.0	wt%
Maleic Anhydride Content	1.3	wt%

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	5.00	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	800	%	ASTM D638, ISO 527-2
Flexural Modulus (Compression Molded)	< 30.0	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	< 40.0	°C	ISO 306/A, ASTM D1525 ¹
Melting Temperature	65.0	°C	ISO 11357-3

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
UBESTA 3012 U	UBE Engineering Plastics, S.A.	Nylon 12	UBESTA
Varcum 29306	Durez Corporation	Phenolic	Varcum
Next Nylon 66 Prime Series PXHS-01BK	Next Polymers Ltd.	Nylon 66	Next Nylon 66 Prime Series
NYCOA Polyamide ASN 27 300 KNF	Nycoa (Nylon Corporation of America)	Nylon 6	NYCOA Polyamide
Pacrel® 6385N	Nanjing Jinling OPTA Polymer Co., Ltd.	TPV	Pacrel®