Ultramid® D3EG10 FC Aqua BK23285
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KxGG9E_Ultramid-D3EG10-FC-Aqua-BK23285.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid® D3EG10 FC Aqua SCHWARZ 23285 is applicable for plastic parts, where the approvals of material for drinking water contact and direct food contact is a mandatory requirement. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.58 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.65 | -- | % | |
| Flow | 0.25 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 120 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.10 | -- | % |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA-GF50 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16000 | 16000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 245 | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 2.5 | % | ISO 527-2 |
| Tensile Creep Modulus 2(1000 hr) | -- | 10300 | MPa | ISO 899-1 |
| Flexural Modulus | 15700 | -- | MPa | ISO 178 |
| Flexural Stress | 350 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 12 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | 95 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/A |
| Melting Temperature | 250 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1100 | -- | J/kg/°C | |
| Thermal Conductivity | 0.34 | -- | W/m/K | DIN 52612 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 320°C (unreinforced) or 330°C (reinforced), TW = 80°C |
| 2 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE ABS 2010CF | Asia International Enterprise (Hong Kong) Limited | ABS | AIE ABS |
| Edgetek™ CY4000-65 NC015 | PolyOne Corporation | PC+PBT | Edgetek™ |
| INEOS LDPE 19N930 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| LUVOCOM® 65-7311 | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |
| Kepital® TX-31 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |