MAJORIS UG500 - 8229
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kw7Opn_MAJORIS-UG500---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS UG500 - 8229 is a special 50 % long glass fibre reinforced polyamide 66 black intended for injection moulding. APPLICATIONS MAJORIS UG500 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.50 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 260 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 16100 | MPa | ISO 178 |
| Flexural Stress | 415 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 59 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 265 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 290 to 305 | °C | |
| Middle Temperature | 285 to 300 | °C | |
| Front Temperature | 280 to 295 | °C | |
| Nozzle Temperature | 275 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 95.0 to 120 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 to 80.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN TR-935 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| EL-Pro™ P700J | SCG Chemicals Co., Ltd. | PP Homopolymer | EL-Pro™ |
| IPC PP 4830H-MLGF8-R2-UV | International Polymers Corporation | PP, Unspecified | IPC PP |
| Petrothene® LR7320 | LyondellBasell Industries | HDPE | Petrothene® |
| TECACOMP® PEEK TRM XS black 4005 | Ensinger GmbH | PEEK | TECACOMP® |