LNP™ STAT-KON™ KE004 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kw3HGa_LNP-STAT-KON-KE004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON KE004 is a compound based on Acetal Copolymer resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound KC-1004 Product reorder name: KE004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 1.6 to 1.8 | % | ASTM D955 |
| Across Flow : 24 hr | 1.7 | % | ISO 294-4 |
| Flow : 24 hr | 0.69 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14500 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 121 | MPa | ASTM D638 |
| Yield | 110 | MPa | ISO 527-2 |
| Break | 121 | MPa | ASTM D638 |
| Break | 110 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.6 | % | ASTM D638 |
| Yield | 1.4 | % | ISO 527-2 |
| Break | 1.6 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11000 | MPa | ASTM D790 |
| -- | 11500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 152 | MPa | ASTM D790 |
| -- | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.9 | J | ASTM D3763 |
| -- | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 162 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 163 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 160 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 160 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5613 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| Nylene® 615SA | Custom Resins Group | Nylon 6 | Nylene® |
| Badamid® A70 GF/GK30 | Bada AG | Nylon 66 | Badamid® |
| Cri-Line GP-715-YW | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| EnCom F0 PC-ABS 9002 | EnCom, Inc. | PC+ABS | EnCom |