Pibiflex® L6060 NAT
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KuuVTp_Pibiflex-L6060-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPC grade with high flexural modulus and high flowing properties |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 70 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 400 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 1 |
| Peak Melting Temperature | 218 | °C | ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4085 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 800 | RTP Company | Acetal (POM) Copolymer | RTP |
| Sindustris POM N110LD | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Nanjing Hongrui PA6 B850 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| POCAN® A 3131 000000 | LANXESS Corporation | PBT+ASA | POCAN® |