TOTAL Polyethylene Lumicene® Supertough 20ST20
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kuhyhf_TOTALPolyethyleneLumiceneSupertough20ST20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lumicene Supertough® 20ST20 is a polyethylene film grade that is especially designed to have an excellent processability in cast extrusion and to give very high "toughness - holding" force balance allowing new innovative multilayer film concepts. Thanks to this innovative design, Lumicene Supertough® 20ST20 allows creation of added value in the film market. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, cast film | 7.80 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, cast film | 7.70 | MPa | ISO 527-3 |
| MD : Fracture, 20 µm, cast film | 37.0 | MPa | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 39.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 20 µm, cast film | 380 | % | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 610 | % | ISO 527-3 |
| Dart Drop Impact (20 µm, Cast Film) | 1100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 20 µm, cast film | 40 | N | ISO 6383-2 |
| TD : 20 µm, cast film | 140 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ISO 306 |
| Melting Temperature | 112 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C | |
| Take-Off Roll | 20 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 10 Z | RTP Company | Nylon 66 | RTP |
| Aaron AVPP 200-1 | Aaron Industries Corp. | PP Homopolymer | Aaron |
| Celcon® M90-07 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| WELLAMID Nylon 6600 GS 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Sylvin 9077-85C Yellow 449 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |