Order Products : sales@su-jiao.com
Advanced Composites BJS-MNR2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Advanced Composites, Inc. |
| Trademark: | Advanced Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KuQSXC_Advanced-Composites-BJS-MNR2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced Composites BJS-MNR2 is a polypropylene product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 - 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 23.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 950 | MPa | ASTM D790 |
| Flexural Strength 4 | 23.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 88.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 | °C | |
| Middle Temperature | 210 - 221 | °C | |
| Front Temperature | 221 | °C | |
| Nozzle Temperature | 216 | °C | |
| Processing (Melt) Temp | 185 - 227 | °C | |
| Mold Temperature | 26.7 - 43.3 | °C | |
| Injection Rate | Slow-Moderate | ||
| Cushion | 5.00 - 10.0 | mm |
| Injection instructions |
|---|
| Screw RPM: 1 to 2 secs before mold openInjection Pressure: 20 to 60% of machine capacity |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5710G30S2 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| Fainplast PVC PK 7075 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Magnobond 92-1 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| Hostacom TRC 333N D82659 | LyondellBasell Industries | PP Copolymer | Hostacom |
| OTECH PVC PL1001-8 - Plenum Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |