GLS PP YN09
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KsdEAN_GLS-PP-YN09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPCP Precolor (unreinforced) |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 to 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 to 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 20.0 to 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 5.0 | % | ASTM D638 |
| Flexural Modulus 3 | 1100 to 1300 | MPa | ASTM D790 |
| Flexural Strength 4 | 25.0 to 30.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 to 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 103 to 107 | °C | |
| 1.8 MPa, Unannealed | 55.0 to 58.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 32.0 to 65.0 | °C | |
| Injection Pressure | 68.0 to 105 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-709H | CHI MEI CORPORATION | ABS | POLYLAC® |
| 3M™ Dyneon™ Fluoroplastic PVDF 32008/0009 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| POLIMAXX SP100 | IRPC Public Company Limited | ABS | POLIMAXX |
| Hypro-G™ PP-CP20 | Entec Polymers | PP Impact Copolymer | Hypro-G™ |
| Kepital® TX-11H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |