LNP™ THERMOCOMP™ AX04518 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KscWXh_LNP-THERMOCOMP-AX04518-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AX04518 is a compound based on ABS resin containing proprietary filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-A-04518 Product reorder name: AX04518 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.67 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6760 | MPa | ASTM D638 |
| -- | 6330 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 78.0 | MPa | ASTM D638 |
| Yield | 74.0 | MPa | ISO 527-2/5 |
| Break 3 | 78.0 | MPa | ASTM D638 |
| Break | 74.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.8 | % | ISO 527-2/5 |
| Break 5 | 1.9 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6260 | MPa | ASTM D790 |
| -- 7 | 5990 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 98.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 112 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 52 | J/m | ASTM D256 |
| 23°C 10 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 11 | 16 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.90 | J | ASTM D3763 |
| -- | 2.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 119 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 120 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 114 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 115 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC30P200-523 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Stat-Tech™ PC-15CF/000 FC BLACK | PolyOne Corporation | PC | Stat-Tech™ |
| BJB Polyurethane F-62 FR A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| EVALENE® LLDPE LF20184 | JG Summit Petrochemical Corporation | LLDPE | EVALENE® LLDPE |
| Kumho KNB 25M | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |