DOMAMID® 6M30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kr390T_DOMAMID-6M30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 30% mineral filler, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(23°C, 72 hr) | 0.90 to 1.1 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 12 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 185 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| Melting Temperature | 218 to 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G3533H-01 | RheTech, Inc. | Nylon 66/6 | Rhelon |
| SPESIN® KP212G15V0W3 | Kolon Plastics, Inc. | PBT | SPESIN® |
| Wondel® A AR0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| Karina BLACK PVC COMPOUND 750-DM-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ QC006 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |