HiFill® PPA GF33 FR HS L is a Polyphthalamide (PPA) product filled with 33% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.8 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 299 | °C | ASTM D648 |
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 21 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 327 to 360 | °C | |
| Middle Temperature | 327 to 360 | °C | |
| Front Temperature | 327 to 360 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8225-65 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Sylvin 2990-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Clariant PC PC-010-L | Clariant Corporation | PC | Clariant PC |
| Elastron® G G400.A65.N | Elastron USA, Inc. | SEBS | Elastron® G |
| MACOMASS PP MM-PP TV 40 | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |