LOFEX® A3111
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KoBInu_LOFEX-A3111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A3111 Polyester film is optically clear and corona treated on both sides with excellent properties by tensile strength , proper elongation and the thermal contraction rate. It can use by release film, laminating film and tape because it has excellent run, easy treatment by suitable product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Tension | |||
| 50.0 µm | 52 | mN/m | |
| 75.0 µm | 52 | mN/m | |
| 100.0 µm | 52 | mN/m |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| F5 | ASTM D882 | ||
| MD : 50.0 µm | 113 | MPa | |
| MD : 75.0 µm | 113 | MPa | |
| MD : 100.0 µm | 113 | MPa | |
| TD : 50.0 µm | 113 | MPa | |
| TD : 75.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 50.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 75.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 50.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 75.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| Surface Treatment | Both sides (Corona) |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.29 | ||
| vs. Itself - Static | 0.32 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 196 | MPa | |
| MD : Yield, 75 µm | 196 | MPa | |
| MD : Yield, 100 µm | 196 | MPa | |
| TD : Yield, 50 µm | 235 | MPa | |
| TD : Yield, 75 µm | 235 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 170 | % | |
| MD : Break, 75 µm | 170 | % | |
| MD : Break, 100 µm | 170 | % | |
| TD : Break, 50 µm | 120 | % | |
| TD : Break, 75 µm | 120 | % | |
| TD : Break, 100 µm | 120 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 50.0 µm | 175 | ||
| 60°, 75.0 µm | 175 | ||
| 60°, 100 µm | 175 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 89.0 | % | |
| 75.0 µm | 89.0 | % | |
| 100 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 1.3 | % | |
| 75.0 µm | 1.5 | % | |
| 100 µm | 1.8 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP7120F B1 | Spartech Polycom | PP, Unspecified | Spartech |
| Celstran® PP-GF30-10 AD 3019 Black | Celanese Corporation | PP, Unspecified | Celstran® |
| Hostaform® EC140XF | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hylon® N2040MGHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| PETILEN YY B 0153 | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |