PALSTYROL® R S 12

Category:	PS (GPPS) , General Purpose Polystyrene
Manufacturer:	pal plast GmbH
Trademark:	PALSTYROL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ko9KCC_PALSTYROL-R-S-12.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALSTYROL®R S 12 is a general-purpose polystyrene product,. It can be processed by injection molding and is available in Europe. Features include: flame retardant/rated flame Good stiffness Transparency

General Information
Features	Rigid, good Good liquidity Definition, high
Appearance	Clear/transparent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.05	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (200°C/5.0 kg)	12.5	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3000	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	42.5	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	2.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	2.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	16	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	82.0	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	375	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 200°C/5 kg: 10 to 15 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2900 to 3100 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 40 to 45 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 1.5 to 3.5 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 14 to 17 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 3 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 84 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³

Additional Information

Melt-Volume Flow Rate, ISO 1133, 200°C/5 kg: 10 to 15 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2900 to 3100 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 40 to 45 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 1.5 to 3.5 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 14 to 17 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 3 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 84 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³

Resin Grade	Manufacturer	Category	Trademark
SUSTAMID 12	Röchling Sustaplast SE & Co. KG	Nylon 12	SUSTAMID
Talcoprene® C530 M8 NATURALE	SO.F.TER. SPA	PP, Unspecified	Talcoprene®
Gallonprene® GP410-6003	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
ISOTHANE® 1160D	Great Eastern Resins Industrial Co Ltd (GRECO)	TPU-Polyester	ISOTHANE®
MAJ'ECO EP287W	AD majoris	PP Copolymer	MAJ'ECO