MarFlex® HHM TR-258
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ko040Q_MarFlex-HHM-TR-258.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex®HHM TR-258 is a linear low density polyethylene material,. This product is available in North America or Latin America. The processing method is: blow molding film or co-extrusion molding. MarFlex®The main features of HHM TR-258 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| Blow film 1 | 0.35 | ASTM D1894 | |
| Blow film 2 | 0.35 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | |||
| 1% secant, MD : 25 µm, blown film 3 | 365 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film 4 | 400 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film 5 | 503 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film 6 | 60.7 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film 7 | 72.4 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film 8 | 45.5 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film 9 | 29.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film 10 | 460 | % | ASTM D882 |
| MD : Broken, 25 µm, blown film 11 | 380 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film 12 | 650 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film 13 | 800 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709 | ||
| 25 µm, blown film 14 | 140 | g | ASTM D1709 |
| 25 µm, blown film 15 | 46 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film 16 | 30 | g | ASTM D1922 |
| MD : 25 µm, blown film 17 | 12 | g | ASTM D1922 |
| TD : 25 µm, blown film 18 | 400 | g | ASTM D1922 |
| TD : 25 µm, blown film 19 | 950 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 60, 25.4 µm, blown film 20 | 40 | ASTM D2457 | |
| 60, 25.4 µm, blown film 21 | 46 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.4 µm, blown film 22 | 36 | % | ASTM D1003 |
| 25.4 µm, blown film 23 | 33 | % | ASTM D1003 |
| Additional Information |
|---|
| Seated buble film preparation 2.5 BUR, 80 mil die gap, 8'' die, 250 lb/hr, 400°F melt temp. High stalk film preparation 4:1 BUR, 40 mil die gap, 8" die, 250 lb/hr, 430°F melt temp. |
| Note Message | |
|---|---|
| 1 . | High Stalk |
| 2 . | Seated Bubble |
| 3 . | High Stalk |
| 4 . | High Stalk |
| 5 . | Seated Bubble |
| 6 . | High Stalk |
| 7 . | Seated Bubble |
| 8 . | High Stalk |
| 9 . | Seated Bubble |
| 10 . | High Stalk |
| 11 . | Seated Bubble |
| 12 . | High Stalk |
| 13 . | Seated Bubble |
| 14 . | High Stalk |
| 15 . | Seated Bubble |
| 16 . | High Stalk |
| 17 . | Seated Bubble |
| 18 . | High Stalk |
| 19 . | Seated Bubble |
| 20 . | High Stalk |
| 21 . | Seated Bubble |
| 22 . | High Stalk |
| 23 . | Seated Bubble |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-257 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Salflex 615TIC | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Ultron® 150C8 | Asia International Enterprise (Hong Kong) Limited | PEI | Ultron® |
| EVICOM™ RC7/025 | INEOS Compounds | PVC, Rigid | EVICOM™ |
| Petrothene® GA594000 | LyondellBasell Industries | LLDPE | Petrothene® |