Infino TK-6036H
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KnUT9l_Infino-TK-6036H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-6036H is a Polyphthalamide (PPA) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 53 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.31 | % | ASTM D955, ISO 2577 |
| Across Flow : 3.20 mm | 0.30 | % | ASTM D955, ISO 294-4 |
| Ash Content | |||
| -- | 41 | % | ASTM D5630 |
| -- | 41 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 116 | ASTM D785 | |
| R-Scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4300 | MPa | ASTM D638 |
| -- | 4010 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 67.0 | MPa | ISO 527-2/5 |
| Break 3 | 65.0 | MPa | ASTM D638 |
| Break | 67.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 2.0 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 5700 | MPa | ASTM D790 |
| -- 6 | 5200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 110 | MPa | ASTM D790 |
| -- 8 | 116 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 0.50 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 23 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 20 | J/m | ASTM D256 |
| 23°C 10 | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 227 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 to 3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 290 to 300 | °C | |
| Middle Temperature | 300 | °C | |
| Front Temperature | 310 | °C | |
| Nozzle Temperature | 320 | °C | |
| Mold Temperature | 130 | °C | |
| Injection Pressure | 118 to 177 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 150 to 250 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC6G25-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| VINIKA® CD75FE | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| UBE Polyamide Elastomer XPA 9063F1 | UBE Industries, Ltd. | TPA-ET | UBE Polyamide Elastomer |
| Hylon® N1033EL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Sylvin 86041-65D Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |