| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KnB00T_Cevian-SAG20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cevian® SAG20 is an Acrylonitrile Butadiene Styrene (ABS) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 68.9 | MPa | ASTM D638 |
| Flexural Modulus | 5860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 105 | °C | ASTM D648 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 31 | kV/mm | ASTM D149 |
| Arc Resistance (3.18 mm) | 67.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (3.18 mm) | 370 | V | UL 746 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.59 mm | 39.0 | ||
| 3.18 mm | 37.0 | ||
| 6.35 mm | 43.0 | ||
| High Voltage Arc Tracking Rate (HVTR) (3.18 mm) | 88.9 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.59 mm | 40 | sec | |
| 3.18 mm | 120 | sec | |
| 6.35 mm | 120 | sec |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 97.9 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207.3 RC HS Black | RTP Company | Nylon 66 | RTP |
| tefanyl® VE VEEP 100 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| 4PROP® 25C1622.5 | 4Plas | PP Copolymer | 4PROP® |
| Amodel® A-4122 HR WH 117 | Solvay Specialty Polymers | PPA | Amodel® |
| Huafon HF-3190A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |