Pearlthane® 11T93
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KmIATI_Pearlthane-11T93.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® 11T93 is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent mechanical properties, including a low compression set value. It is specially designed for injection moulding, exhibiting a fast cycle time. Pearlthane® 11T93 is especially recommended for injection moulding applications, such as: automotive parts, seals and gaskets, shoe soles and a variety of high performance technical parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| 20°C | 1.16 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 93 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 9.00 | MPa | ASTM D412, ISO 527 |
| 300% strain | 17.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 500 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 120 | kN/m | ASTM D624 |
| -- | 120 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 34 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -47.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 197 - 207 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 35.0 | °C |
| Injection instructions |
|---|
| Closing force: : 30 tonsScrew diameter: : 30 mmMaximum hydraulic pressure: : 210 bar.Mould Plaque 120x120x2 mmL/D ratio: : 23 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO T1202 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Toraypef® 15020 AP61 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Braskem PP H 158 | Braskem | PP Homopolymer | Braskem PP |
| Durethan® BM 430 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| Jamplast JPLGABSI | Jamplast, Inc. | ABS | Jamplast |