LNP™ LUBRILOY™ D20009 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KlsX9D_LNP-LUBRILOY-D20009-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D20009 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Flame Retardant, Wear Resistant. Also known as: LNP* LUBRILOY* Compound D-FR Product reorder name: D20009 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 84 | % | ASTM D638 |
| Flexural Modulus | 2290 | MPa | ASTM D790 |
| Flexural Strength | 87.1 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.13 | ||
| Wear Factor - Washer | 56.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 700 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-2 | ||
| 3.00 mm, Testing by SABIC | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 304 to 316 | °C | |
| Processing (Melt) Temp | 304 to 316 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE DM500 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Nanjing Hongrui PC CS500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| GERMAMID 6 EX | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| INLUBE PBTCF15TF15 | Infinity LTL Engineered Compounds | PBT | INLUBE |
| LNP™ COLORCOMP™ 143RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |