Vandar® 2122
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Vandar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KlhCWV_Vandar-2122.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vandar 2122 is a polyester alloy which contains 10% mineral filler. It offers exceptional toughness and practical impact strength. This resin offers Class A paintable finish with excellent dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.3 - 1.5 | % | ASTM D955 |
| Vertical flow direction | 1.3 - 1.5 | % | ISO 294-4 |
| Flow direction | 1.3 - 1.5 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 44.1 | MPa | ASTM D638 |
| 50% strain | 30.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Fracture, 23°C | 80 | % | ASTM D638 |
| Fracture | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 128 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 132 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 96.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKALOY™ T80HI | Mando Advanced Materials Co., Ltd. | ABS+PBT | TEKALOY™ |
| CP PRYME® Polypropylene PPC100-20M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Hax™ HFX 035/3 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Keltan® 6950C | LANXESS Buna GmbH | EPDM | Keltan® |
| Sylvin 9600-95 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |