LNP™ THERMOCOMP™ 5E003M compound
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KlHL1x_LNP-THERMOCOMP-5E003M-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 5E003M is a compound based on PVDF resin containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-VC-1003 M Product reorder name: 5E003M |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9060 | MPa | ASTM D638 |
| -- | 7460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/5 |
| Break 3 | 47.0 | MPa | ASTM D638 |
| Break | 46.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/5 |
| Break 5 | 6.8 | % | ASTM D638 |
| Break | 6.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 5470 | MPa | ASTM D790 |
| -- 7 | 6590 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 79.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 79.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 9 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 10 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.0 | J | ASTM D3763 |
| -- | 3.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 160 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 114 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 225 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 215 to 230 | °C | |
| Mold Temperature | 65.0 to 90.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 3645 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Yuyao PBT 3060G30 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| Network Polymers SMMA MS 100 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| BP Flex 8000 VP BLK | Buckeye Polymers, Inc. | TPE | BP Flex |
| Epolene® N-14 | Westlake Chemical Corporation | LDPE | Epolene® |