LNP™ LUBRICOMP™ WFI14 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kl634k_LNP-LUBRICOMP-WFI14-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Lubricomp* WFI14 is a compound based on Polybutylene Terephalate resin containing Glass Fiber and silicone. Added Features include: internally lubricated. Also known as: LNP* LUBRICOMP* Compound WFI14 Product reorder name: WFI14 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 98.0 | MPa | |
| Break | 99.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 4.1 | % | |
| Break | 4.3 | % | |
| Flexural Modulus 1 | 5600 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 149 | MPa | |
| -- 4 | 126 | MPa | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.36 | ASTM D3702 Modified | |
| Flexural Strain at Break 5 | 4.3 | % | ISO 178 |
| Wear Factor - Washer | 113 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(0.45 MPa, Unannealed, 64.0 mm Span) | 217 | °C | ISO 75-2/Bf |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.3E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarFlex P 7380-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| Xuchuan XCS-150P | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DJSilicone NE-681 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Diablend 4500 | DTR S.r.l. (Develop Thermoplastic Resins) | PC+ABS | Diablend |
| LAMIGAMID® 510 | Schwartz Technical Plastic | PET | LAMIGAMID® |