LNP™ THERMOCOMP™ WF0039U compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kkplh2_LNP-THERMOCOMP-WF0039U-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WF0039U is a compound based on PBT resin containing 15% Glass Fiber. Added features of this grade include: Flame Retardant and UV Stabilized. Also known as: LNP* THERMOCOMP* Compound WF-1003 FR-S UV Product reorder name: WF0039U |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7240 | MPa | ASTM D638 |
| -- | 7080 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 95.0 | MPa | ASTM D638 |
| Break | 95.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.4 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6060 | MPa | ASTM D790 |
| -- 5 | 6360 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 145 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 7 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D4812 |
| 23°C 8 | 20 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.70 | J | ASTM D3763 |
| -- | 1.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 215 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 212 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 194 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 185 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 243 to 260 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REDI-LINK™ DFDA-5430 NT | The Dow Chemical Company | LLDPE | REDI-LINK™ |
| Ultraform® H 2320 004 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Unichem 8605 | Colorite Polymers | PVC, Unspecified | Unichem |
| HyTemp® 4051EP | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| Durethan® BKV 15 000000 | LANXESS GmbH | Nylon 6 | Durethan® |