PENTAMID B GV30 E H schwarz
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KkXXai_PENTAMID-B-GV30-E-H-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 6, 30% glass fiber reinforced, impact modified |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.65 | -- | % | ISO 294-4 |
| Flow direction | 0.40 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 185 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 5100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.8 | 7.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 31 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.90 | -- | IEC 60250 | |
| Comparative Tracking Index | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA6-HI, MHRC, 14-090 N, GF30The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA6-HI, MHRC, 14-090 N, GF30Unnotched Charpy Impact, ISO 179, 23°C, Type 1, Edgewise: >100 kJ/m² |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.090 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 260 - 285 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 75.0 | MPa | |
| Holding Pressure | 45.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® 3025U(H) | Samyang Corporation | PC | TRIREX® |
| Utomer UT1CP90A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| ACCUTECH™ CP0437C40L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| LNP™ LUBRICOMP™ RFL22E compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Plaslube® J-4/30/TF/13/SI/2 NAT | Techmer Engineered Solutions | Nylon 612 | Plaslube® |