Rilsan® HT CESV BLACK P010-HP TL
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kk5ULd_Rilsan-HT-CESV-BLACK-P010-HP-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CESV BLACK P010-HP TL is a flexible polyphthalamide produced from a renewable source, typically used to replace metal in tubing for high-temperature automotive, transportation and other demanding technical applications requiring high burst resistance. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1580 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 48.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.5 | % | |
| Break | > 100 | % | |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 11 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 55 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Melt Temperature | 270 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILOY® TP210T | Samyang Corporation | PC+ABS | TRILOY® |
| FLEXCHEM™ 6051-02 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Iupiace® TX403 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LNP™ LUBRICOMP™ YL003 compound | SABIC Innovative Plastics | TPEE | LNP™ LUBRICOMP™ |
| LEXAN™ EXL1890T resin | SABIC Innovative Plastics | PC | LEXAN™ |