RAMTAL PM8103NT7
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTAL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KiRZ8o_RAMTAL-PM8103NT7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Acetal Copolymer, Impact Modified, for Injection Moulding applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.3 to 1.7 | % | ASTM D955 |
| -- | 1.3 to 1.7 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1670 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 12 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 55.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 115 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 166 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 15 | mm/min | FMVSS 302 |
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alpha PVC GW 3010 NATURAL LCF-P | AlphaGary | PVC, Unspecified | Alpha PVC |
| Clyrell RC5004 | HMC Polymers | PP Random Copolymer | Clyrell |
| DynaMix™ 2035-L | Polymer Dynamix | Nylon 66 | DynaMix™ |
| LNP™ LUBRICOMP™ UX05051 compound | SABIC Innovative Plastics Europe | PPA | LNP™ LUBRICOMP™ |
| Cellasto® MH24-40 | BASF Polyurethanes GmbH | TPU, Unspecified | Cellasto® |